AWS/ASME SFA - 5.18

ER70S-3

EN ISO 14341 - A

G 38 3 C1 G 2Si

EN ISO 14341 - A

G 38 3 M21 G 2Si

TS EN ISO 14341 - A

G 38 3 C1 G 2Si

TS EN ISO 14341 - A

G 38 3 M21 G 2Si

DIN M. No.

1.5112

Unalloyed wire electrode for GMA (MIG/MAG) welding of unalloyed steels by using CO2 or mixed gases, depending on thickness of the base metal. Characterized by a reduced slag formation and smooth welding deposit. Particularly suitable for welding of galvanized and pre-paint steels, welding unalloyed steels in pipe-lines, boilers and tank construction. Suitable also welding thin metal plates and repair welds. A thin and homogeneous copper coating increases electrical conducvitiy and protects the wire from using.

AWS/ASME SFA - 5.18

ER70S-6

EN ISO 14341 - A

G 42 3 C1 G 3Si1

EN ISO 14341 - A

G 42 4 M21 G 3Si1

TS EN ISO 14341 - A

G 42 3 C1 G 3Si1

TS EN ISO 14341 - A

G 42 4 M21 G 3Si1

DIN M. No.

1.5125

Unalloyed wire electrode for GMA (MIG/MAG) welding of general structural steels, pipe steels, and cast steels using CO2 or mixed shielding gases, depending on thickness of hte base metal. Generally used in steel construction, shipbuilding, machine, tank, boiler production, automotive industry. Preheating is required, depending on the plate thickness and carbon equivalent of the base metal. A thin and homogeneous copper coating increases electrical conductivity and protects the wire from rusting.

AWS/ASME SFA - 5.18

ER70S-6

EN ISO 14341 - A

G 46 4 M21 G 4Si1

EN ISO 14341 - A

G 46 4 C1 G 4Si1

TS EN ISO 14341 - A

G 46 4 C1 G 4Si1

TS EN ISO 14341 - A

G 46 4 M21 G 4Si1

DIN M. No.

1.5130

Unalloyed wire electrode for GMA (MIG/MAG) welding of general structural steels, pipes and cast steels by using CO2 or mixed shielding gases can be used depending on thickness of the base metal. Generally used in steel construction, machine, tank, boiler production. Preheating is required, depending on the plate thickness and carbon equivalent of the base metal. A thin and homogeneous copper coating increases electrical conductivity and protects the wire from rusting.

AWS/ASME SFA - 5.18

ER70S-6

EN ISO 14341 - A

G 42 4 M21 3Si1

EN ISO 14341 - A

G 42 4 C1 3Si1

TS EN ISO 14341 - A

G 42 4 M21 3Si1

TS EN ISO 14341 - A

G 42 4 C1 3Si1

DIN M. No.

1.5125

Non-copper coated and unalloyed GMA (MIG/MAG) wire electrode, especially produced for welding without spatter or very low level of spatter. Suitable for welding of general structural steels, boiler steels, pipe steels and cast steels. Due to it's special coating provides stable arc and no spatter especially with mixed shielding gases which can be used depending on the thickness. Generally preferred in robotic applications, due to it's high welding performance without spatter and cleaning needs. Also provides cost advantages in cleaning after welding, torch spare part consumptions like, contact tip, spiral, driving wheel, anti-spatter sprey. Due to these advantages preferably used in automotive, machine and steel furniture production.

AWS/ASME SFA - 5.18

ER70S-6

EN ISO 14341 - A

G 46 4 M21 G 4Si1

EN ISO 14341 - A

G 46 4 C1 G 4Si1

TS EN ISO 14341 - A

G 46 4 M21 G 4Si1

TS EN ISO 14341 - A

G 46 4 C1 G 4Si1

DIN M. No.

1.5130

Non-copper coated and unalloyed GMA (MIG/MAG) wire electrode, especially produced for welding without spatter or very low level of spatter. Suitable for welding of general structural steels, boiler steels, pipe steels and cast steels. Due to it's special coating provides stable arc and no spatter especially with mixed shielding gases which can be used depending on the thickness. Generally preferred in robotic applications due to it's high welding performance without spatter and cleaning needs. Also provides cost advantages in cleaning after welding, torch spare part consumptions like, contact tip, spiral, driving wheel, anti-spatter sprey. Due to these advantages preferably used in automotive, machine and steel furniture production.

AWS/ASME SFA - 5.18

ER70S-2

EN ISO 14341 - A

G 42 3 C1 G 2Ti

EN ISO 14341 - A

G 42 3 M21 G 2Ti

TS EN ISO 14341 - A

G 42 3 C1 G 2Ti

TS EN ISO 14341 - A

G 42 3 M21 G 2Ti

Micro-alloyed wire electrode for GMA (MIG/MAG) welding of unalloyed and low-alloy steels. Characterized by a reduced slag formation and smooth welding deposit. Due to its Al and Ti micro-alloy content, particularly suitable for single pass welding of galvanized, pre-painted, rusty and dirty steels, welding low alloy steels in pipe-lines, boilers and tank production. Suitable also welding in thin metal plates and repair welds. CO2 or mixed shielding gases can be used depending on the thickness of the base metal. A thin and homogeneous copper coating increases electrical conductivity and protects the wires from rusting.