AWS/ASME SFA - 5.3

E1100

EN ISO 18273

E Al 1080 A(Al 99.8)

TS EN ISO 18273

E Al 1080 A(Al 99.8)

TS 9604

EL-Al99.5

DIN M. No.

3.0286

Special coated electrode for welding pure aluminium. Weld metal has good color matching with base metal and high electrical conductivity. Hold the electrode perpendicularly to workpiece, with a short arc length, during welding. If the thickness is greater than 10 mm or in large workpieces, preheating shall be applied between 150°C to 250°C. Since slag residues are corrosive, they must be completely removed from the weld bead. Electrode serves well as consumable in oxyacetylene welding. The covering being hygroscopic, electrodes must be stored in an absolutely dry location, or redried if required.

AWS/ASME SFA - 5.3

E4043

EN ISO 18273

E Al 4043 (AlSi 5)

TS EN ISO 18273

E Al 4043 (AlSi 5)

TS 9604

EL-AlSi5

DIN M. No.

3.2245

Special coated electrode for welding aluminium-silicon alloys and for joining dissimilar aluminium alloys. Suitable to use also in aluminium castings, containing up to 5% silicon. Used with DCEP. Hold the electrode perpendicularly to workpiece, with a short arc length, during welding. If the thickness is greater than 10 mm or in large workpieces, preheating shall be applied between 150°C to 250°C. Since slag residues are corrosive, they must be completely removed from the weld bead. Electrode serves well as consumable in oxyacetylene welding. The covering being hygroscopic, electrodes must be stored in an absolutely dry location, or redried if required.

AWS/ASME SFA - 5.3

E4047

EN ISO 18273

E Al 4047 (AlSi 12)

TS EN ISO 18273

E Al 4047 (AlSi 12)

TS 9604

EL-AlSi12

DIN 1732

EL-AlSi12

DIN M. No.

3.2585

Special coated electrode for aluminium-silicon and aluminium-magnesium-silicon castings. Suitable to use also in aluminium castings, containing up to 12% silicon. Used with DCEP. Hold the electrode perpendicularly to workpiece, with a short arc length, during welding. If the thickness is greater than 10 mm or in large workpieces, preheating shall be applied between 150°C to 250°C. Since slag residues are corrosive, they must be completely removed from the weld bead. Electrode serves well as consumable in oxyacetylene welding. The covering being hygroscopic, electrodes must be stored in an absolutely dry location, or redried if required.