AWS/ASME SFA - 5.11

ENiCrFe-3

EN ISO 14172

E Ni 6182

TS EN ISO 14172

E Ni 6182

DIN M. No.

2.4620

Basic coated electrode with Ni-Cr-Fe type nickel base deposit. Used for repairing and joining of nickel alloys, 5 - 9% Nickel steels, cryogenic stainless steels down to -196°C, Incoloy 800 and other high temperature steels. Provides a weld metal which has a operating temperatures from -196°C to 800°C. Used for joining dissimilar materials as stainless steels/low alloyed steels, stainless steels/Nickel alloys, buffering of difficult to weld steels. Weld metal deposit is insensitive to cracks, has very good resistance to acids, salts and alkaline solutions, molten salt (e.g. cyanide) in oxidizing and carburization atmospheres (avoid a sulphurous atmosphere). Generally used for welding on oven parts, burners, heat treatment equipment, cement works, moulds, transport and storage tanks of liquid gas. Has a wide range of application in chemical industry, petrochemical industry, glassworks, civil engineering, repairing and maintenance workshops.

AWS/ASME SFA - 5.11

~ENiCrMo-4

EN ISO 14172

E Ni 6275

TS EN ISO 14172

E Ni 6275

DIN 8555

E 23-UM-200-CZKT

Heavy coated, high recovery (170%) surfacing and hard surfacing electrode which gives Nickel-Chromium-Molibdenum alloy weld metal. Weld metal is resistant to abrasion, impact, corrosion and high temperatures. Especially used in welding of hot-work press tools which are subjected to above service conditions. Suitable to use inmaintenance welding of hot-work press tools and hammers, forging and extrusion dies and parts, pressure casting pistons and dies, rolling rolls, hot-stripping tools, pump rotors and valves. Preheating to 400-500°C is required, depending on the size, shape and chemical analysis of the part to be welded. Has a stable arc, smooth weld bead surface and weld metal is free of cracks and porosity. Welding shall be performed with short stick-out distance, perpendicular to base metal and craters shall be filled well. Preferred to use with DC, electrode in positive (+) and possible to use also in AC.

AWS/ASME SFA - 5.11

ENiCu-7

EN ISO 14172

E Ni 4060

TS EN ISO 14172

E Ni 4060

DIN M. No.

2.4366

Electrode having monel core wire, designed for joining and surfacing welds of Monel-clad steels. Suitable for joining Monel alloys to steel; weld surfacing of steel with corrosion-resistant Monel coating. The weld metal is free of porosity and resistant to many chemicals. Suitable for applications with working temperatures from -196°C to 450°C. Weld groove preparation and cleaning should be done carefully. Generally welding should be done in horizontal position with short stick-out distance without weaving. Due to porosity risk of the weld metal, welding and striking shall be started on end plate. Possible to use with DCEP.