FCH 330

Standards

EN 14700 T Fe1
TS EN 14700 T Fe1
DIN 8555 MF 1-GF-300-P

Properties and Applications

Gas shielded flux cored wire which is developed for hardfacing of parts subjected to metal-to-metal friction wear (adhesion) and medium degree impacts. Due to it's very tough and crack resistant weld metal, it is also used for buffer layer applications. As the weld metal has medium degree of hardness it can be machined by chip forming and flame or inductive hardening is possible. Interpass temperature should not exceed 250°C, during welding.

Typical Applications : Hardfacing torque gears, gear wheels, shafts, pallet reels, crane wheels, pulleys, railway rails, crossings and switch points, rollers, caterpillar tracks, sprockets, track links, gears, shafts, pinion gears in sugar industry, screws in oil industry, crane drums and wheels, mine car wheels and sheaves.
Fch 330 Sert Dolgu

Wear Resistance Types


Abrasion

Adhesion

Impact

Temperature

Corrosion
Low
Medium
High
Very High

Typical Applications

Fch 330 Model Tipik Uygulamalar Fch 330 Model Tipik Uygulamalar Fch 330 Model Tipik Uygulamalar Fch 330 Model Tipik Uygulamalar

Typical Chemical Values of Weld Metal

Type of AnalysisCSiMnCrFe
Weld Deposit0.200,501.301.6096.40

Typical Mechanical Values of Weld Metal(%)

Test ConditionProtection GasHardness (HB)
As weldedC1300

* Chemical compositon and mechanical properties are valid when using shielding gas EN ISO 14175 - C1 (%100 CO2) .

Application Information

Welding Positions :
Fch 330 Kaynak Pozisyonu Fch 330 Kaynak Pozisyonu

Polarity:

Fch 330 Kutuplama DC(+)

Protection Gas:

M21 C1

Welding Parameters & Efficiency :

Diameter (mm)Deposition Rate(kg/h)Efficiency(%)
1.202.1395
1.602.7994
2.404.9993

Packaging Information

Product CodeDiameter (mm)Weight Of The Box (kg)Boxes Per PackageWeight Of The PackagePackaging Type
38000EJAM21.2015.0115.7Wire Basket Spool (K300MS)
38000GJAM21.6015.0115.7Wire Basket Spool (K300MS)
38000IXAM22.4025.0125.8Wire Basket Spool (K435)

Storage & Re-Drying Information

>Shouldn t be exposed to high statical load and impact.