EM 296

Datasheet

Standards

AWS/ASME SFA - 5.5	E9015-B92 H4R
EN ISO 3580 - A	E ZCrMoWVNb9 0.5 2 B 32 H5
TS EN ISO 3580 - A	E ZCrMoWVNb9 0.5 2 B 32 H5

Properties And Applications

Designed for welding P92 steels used in high-temperature applications such as power plants, refineries, and gasification facilities, these consumables are resistant to service temperatures up to 650?°C. Cr-Mo-Ni-V-W-Nb alloyed and offer stable arc performance, low spatter, easy slag removal, and low-hydrogen weld metal characteristics.

Typical Chemical Values of Weld Metal

Type of Analysis	C	Si	Mn	Cr	Ni	Mo	V	W
Weld Deposit	0.10	0.20	0.80	9.50	0,50	0,50	0.20	1.80

Type of Analysis

Weld Deposit

0.10

0.20

0.80

9.50

0,50

0.20

1.80

Typical Mechanical Values of Weld Metal(%)

Test Condition	Yield Strength (N/mm²)	Tensile Strength (N/mm²)	Elongation A5 (%)	Charpy V-Notch Properties (J)
After Heat Treatment(760°C 2 hour)	620	730	22	20°C → 45

Test Condition

Yield Strength (N/mm²)

Tensile Strength (N/mm²)

Elongation A5 (%)

Charpy V-Notch Properties (J)

After Heat Treatment(760°C 2 hour)

620

730

20°C → 45

Application Information

Welding Positions :

Polarity:

DC(+)

Welding Parameters & Efficiency :

Diameter x Length (mm)	Current (A)
3.25x350	90-130

Diameter x Length (mm)

Current (A)

3.25x350

90-130

Packaging Information

Product Code	Diameter X Length (mm)	Pieces per Box (~)	Weight Of The Box (kg)	Boxes Per Package	Weight Of The Package	Packaging Type
12040NREM2	3.25x350	138	5.0	3	15.4	Cardboard Box

Storage & Re-Drying Information

>It can be dried maximum 5 times.

>It has to be dried at 350°C for 2 hours.