ENI 416 (NiFe)

Standards

AWS/ASME SFA - 5.15 ENiFe-CI
EN ISO 1071 E C NiFe-CI 3
TS EN ISO 1071 E C NiFe-CI 3

Materials

DIN
GGG 40.3 - GGG 70
GTS 35-10 - GTS 70-02
GTW 35-04 - GTW S 38-12

Properties and Applications

Electrode having a nickel-iron core wire, for welding cast iron with or without preheating. The weld metal features a low coefficient of thermal expansion and as a result, little shrinkage. It has higher strength properties than pure nickel weld metal and is therefore preferably used for welding nodular cast iron, white and black heart malleable cast iron, as well as austenitic nodular cast iron or joining these metals to components made of steel, copper or nickel materials. Easy arc striking and restriking, stable arc, smooth bead. Weld metal is machinable. Weld short beads.
Eni 416 (NiFe) Sert Dolgu

Typical Chemical Values of Weld Metal

Type of AnalysisCSiMnNiAlFe
Weld Deposit0.451.600.6552.000.8044.50

Typical Mechanical Values of Weld Metal(%)

Test ConditionHardness (HB)
As welded210

Application Information

Welding Positions :
Eni 416 (NiFe) Kaynak Pozisyonu Eni 416 (NiFe) Kaynak Pozisyonu Eni 416 (NiFe) Kaynak Pozisyonu Eni 416 (NiFe) Kaynak Pozisyonu Eni 416 (NiFe) Kaynak Pozisyonu Eni 416 (NiFe) Kaynak Pozisyonu

Polarity:

Eni 416 (NiFe) Kutuplama Eni 416 (NiFe) Kutuplama

Welding Parameters & Efficiency :

Diameter x Length (mm)Current (A)
2.50x30050-80
3.25x30080-110
4.00x400110-140

Packaging Information

Product CodeDiameter x Length (mm)Quantity per BoxBox Gross Weight (kg)Boxes per Outer BoxOuter Box Gross Weight (kg)Packaging Type
16003GBEM22.50x30060 pcs1.10100.00 
16003GDEM22.50x300160 pcs2.6238.00Plastic Box
16003GJEM22.50x300112 pcs1.791018.20VAC Box
16003M9EM13.25x30015 pcs0.333511.60Blister
16003MBEM23.25x30037 pcs1.111011.30 
16003MDEM23.25x30093 pcs2.6238.00Plastic Box
16003MJEM23.25x30065 pcs1.791018.20VAC Box
16003RBEM24.00x40032 pcs0.00100.00 
16003RJEM24.00x40048 pcs2.55923.10VAC Box

Storage & Re-Drying Information

>It can be dried maximum 5 times.
> It has to be dried at 150°C for 1 hour.