FCO 540

Standards

EN 14700 T Fe16
TS EN 14700 T Fe16
DIN 8555 MF 10-GF-65-GRZ

Properties and Applications

Open-arc flux cored wire, designed to resist high stress grinding abrasion and solid erosion at service temperatures up to 600°C. Deposits weld metal which is contains Cr, Nb, Mo alloys with addition of W and V carbides. Hardfacing shall not exceed 6 mm in heigth. Weld metal is machinable by grinding. The deposit will readily stress relief check crack which is not detrimental to abrasion resistance.

Typical Applications: Hardfacing wear plates, sinter plant parts, exhaust fan blades in pellet plants, pearlite crushers, bucket teeth and lips on bucket-wheel excavators in phosphate mines, boiler fan blades in sugar cane industry, burden area in blast furnace bells, wear plates in blast furnace belless top charging systems.
Fco 540 Sert Dolgu

Wear Resistance Types and Microstructure


Abrasion

Adhesion

Darbe

Temperature

Corrosion
Düşük
ORTA
Yüksek
Çok Yüksek

Typical Applications

Fco 540 Model Tipik Uygulamalar Fco 540 Model Tipik Uygulamalar Fco 540 Model Tipik Uygulamalar Fco 540 Model Tipik Uygulamalar

Typical Chemical Values of Weld Metal

Type of AnalysisCSiMnCrMoVWNbFe
Weld Deposit5.000.550.2022.006.400.701.606.0057.55

Typical Mechanical Values of Weld Metal(%)

Test ConditionHardness (HRc)Wear Index
As welded644.5

Application Information

Welding Positions :
Fco 540 Kaynak Pozisyonu Fco 540 Kaynak Pozisyonu

Polarity:

Fco 540 Kutuplama

Welding Parameters & Efficiency :

Diameter (mm)Yığma Oranı(kg/saat)Verimlilik(%)
2.404.2191
2.807.7492

Packaging Information

Product CodeDiameter (mm)Kutudaki Miktar (yakl)Kutu Net Ağırlığı (kg)Number Of Boxes In PackageKoli Net Ağırlığı (kg)Packaging Type
38211GJAM21.6015 kg15.0115.7Wire Basket Spool (K300MS)
38211IJAM22.4015 kg15.0115.7Wire Basket Spool (K300MS)
38211IXAM22.4025 kg25.0125.8Wire Basket Spool (K435)
38211JXAM22.8025 kg25.0125.8Wire Basket Spool (K435)

Storage & Re-Drying Information

>Shouldn t be exposed to high statical load and impact.