SHF 325

Standards

EN ISO 14174 S A CS 3
TS EN ISO 14174 S A CS 3

Properties and Applications

Alloyed and agglomerated flux, which is designed for submerged arc hardfacing of parts subjected to metal to metal friction wear, moderate impart and low stress mineral abrasion. Provides weld metal with 225-300 HB hardness, when used with SW 702 wire electrode. Possible to use in direct current. Hardness and transfer of alloying elements to the weld metal depens on welding parameters used. For instance, optimum welding parameters for 4.00 mm wire electrode are about 600 A, 32 V, 50 cm/min. welding speed. Gives very smooth and clean weld bead surfaces, slag removal is very easy and generally slag is self releasing.

Typical Applications: Suitable for hardfacing of machine gear parts, rails, supports rolls of caterpillars, pulleys, locomotive wheels, table and support rolls in iron and steel industry.
Shf 325 Sert Dolgu

Dayanım Gösterdiği Aşınma Tipleri ve Mikroyapısı


Abrasion

Adhesion

Darbe

Temperature

Corrosion

Typical Applications

Shf 325 Model Tipik Uygulamalar Shf 325 Model Tipik Uygulamalar Shf 325 Model Tipik Uygulamalar Shf 325 Model Tipik Uygulamalar

Typical Chemical Values of Weld Metal

Welding WireType of AnalysisCSiMnCrMo
SW 702Weld Deposit0.150.601.501.000.25

Typical Mechanical Values of Weld Metal(%)

Test ConditionWelding WireHardness (HB)Hardness (HRc)
As weldedSW 702225-30020 - 32

Application Information

Welding Positions :
Shf 325 Kaynak Pozisyonu Shf 325 Kaynak Pozisyonu

Polarity:

Shf 325 Kutuplama Shf 325 Kutuplama

Welding Parameters & Efficiency :

Packaging Information

Product CodeQuantity per BoxBox Gross Weight (kg)Boxes per Outer BoxOuter Box Gross Weight (kg)Packaging Type
408010AGM225 kg25.60125.60Kraft Bag

Storage & Re-Drying Information

>Generally not required. If required, redry for 1 hour at 110°C.
>During transportation and storage, it should be ensured that the packaging is not damaged or torn.
>It has to be dried at 350°C for 2 hours.