SHF 335

Standards

EN ISO 14174 S A CS 3
TS EN ISO 14174 S A CS 3

Properties and Applications

Alloyed and agglomerated flux, which is designed for submerged arc hardfacing of parts subjected to metal to metal friction wear, moderate impart and low stress mineral abrasion. Provides weld metal with 325-400 HB hardness, when used with SW 702 wire electrode. Possible to use in direct current. Hardness and transfer of alloying elements to the weld metal depens on welding parameters used. Gives very smooth and clean weld bead surfaces, slag removal is very easy and generally slag is self releasing.

Typical Applications : Hardfacing of pinch rollers, table rolls, idlers, couplings, piston rod ends.
Shf 335 Sert Dolgu

Dayanım Gösterdiği Aşınma Tipleri ve Mikroyapısı


Abrasion

Adhesion

Darbe

Temperature

Corrosion

Typical Applications

Shf 335 Model Tipik Uygulamalar Shf 335 Model Tipik Uygulamalar Shf 335 Model Tipik Uygulamalar Shf 335 Model Tipik Uygulamalar

Typical Chemical Values of Weld Metal

Welding WireType of AnalysisCSiMnCrMo
SW 702Weld Deposit0.200.651.502.000.45

Typical Mechanical Values of Weld Metal(%)

Test ConditionWelding WireHardness (HB)Hardness (HRc)
As weldedSW 702325 - 40033 - 40

Application Information

Welding Positions :
Shf 335 Kaynak Pozisyonu Shf 335 Kaynak Pozisyonu

Polarity:

Shf 335 Kutuplama Shf 335 Kutuplama

Welding Parameters & Efficiency :

Packaging Information

Product CodeQuantity per BoxBox Gross Weight (kg)Boxes per Outer BoxOuter Box Gross Weight (kg)Packaging Type
408040AGM225 kg25.60125.60Kraft Bag

Storage & Re-Drying Information

>Generally not required. If required, redry for 1 hour at 110°C.
>During transportation and storage, it should be ensured that the packaging is not damaged or torn.
>It has to be dried at 350°C for 2 hours.