TI 630

Standards

AWS/ASME SFA - 5.9 ER630
EN ISO 14343 - B SS630
DIN M. No. 1.4542

Properties And Applications

GTA (TIG) welding rod for welding of 17Cr/4 Ni containing, 630 (1.4542) and similar precipitation hardening-martensitic stainless steels. Especially used in hydraulic equipment components, impellers, pump shafts, valves which are exposed to high corrosion in petrochemical industry, chemical plants. In order to gain precipitation hardening martensitic steel properties of the the weld metal after welding, solution heat treatment shall be done at 1052°C (±28°C) to have austenite matrix, then quenching to 149-93°C to transform the matrix to martensite and then precipitation/aging heat treatment at 482-621°C for 4 hours. After precipitation hardening heat treatment, weld metal has very high mechanical strength and high toughness, as well as very good corrosion and oxidation resistance. MIG/MAG Welding Wire: MI 630

Materials

Width Material
X5CrNiCuNb17-4-4 1.4542

Typical Chemical Features of the Welding Wire

Type of AnalysisCSiMnCrNiNbCu
Welding Wire0.020.400.4016.254.700.223.40

Typical Mechanical Values of Weld Metal(%)

Test ConditionProtection GasYield Strength (N/mm²)Tensile Strength (N/mm²)Elongation A5 (%)Charpy V-Notch Properties (J)
Isıl İşlem Sonrası (1050°C 1 Saat)I19801020170°C → 100-20°C → 70

* Chemical compositon and mechanical properties are valid when using shielding gas .

Application Information

Welding Positions :
Ti 630 Kaynak Pozisyonu Ti 630 Kaynak Pozisyonu Ti 630 Kaynak Pozisyonu Ti 630 Kaynak Pozisyonu Ti 630 Kaynak Pozisyonu Ti 630 Kaynak Pozisyonu

Polarity:

Ti 630 Kutuplama

Protection Gas:

I1

Welding Parameters & Efficiency :

Diameter x Length (mm)
1.60x1000
2.00x1000
2.40x1000

Packaging Information

Product CodeDiameter x Length (mm)Quantity per BoxBox Gross Weight (kg)Boxes per Outer BoxOuter Box Gross Weight (kg)Packaging Type
23114GBKM21.60x10005 kg5.30421.40Cardboard Tube
23114HBKM22.00x10005 kg5.30421.40Cardboard Tube
23114IBKM22.40x10005 kg5.30421.40Cardboard Tube