Flux Cored Wires

EN 14700

T Z Fe8

TS EN 14700

T Z Fe8

DIN 8555

MF 3-GF-50-CT

It is used in repair and maintenance welding of parts exposed to high temperature, corrosion, metal-to-metal friction and impact.  The weld metal has a high content of Co, Cr, Mo alloys and is used for the wear repair of steels operating at temperatures up to 650°C. It has a stable arc and a smooth weld seam. Typical Applications: Continuous casting rolls, rolls, forging dies, forming and punching tools, pumping equipment, punching tools

EN 14700

T Fe3-40-M21

EN 14700

T Fe3-40-M13

DIN 8555

MF 3-GF-40-PT

EN 14700

~T Fe7

TS EN 14700

~T Fe7

DIN 8555

MF-5-GF-250-C

Open arc flux cored wire for surfacing and buffer layer application on parts, subjected to metal-to-metal wear (adhesion), moderate impact, thermal fatigue and corrosion. Especially designed for buffer layer application, in order to reduce dilution and crack suseptibility of new continue casting rollers, at the top part of the line. Provides smooth and easily machinable surface on stringer weld bead or weaving technique.Typical Applications: Suitable for buffer layer on new continue casting rolls, before hardfacing layers. Also suitable for surfacing of steam turbines, valves and valve seats.

EN 14700

T Fe4

TS EN 14700

T Fe4

DIN 8555

MF 3-GF-60-ST

It is a hardfacing welding wire used for hardfacing welding of parts exposed to metal-to-metal friction wear, pressure, and impact at high temperatures. The weld metal exhibits high strength, toughness, and heat resistance. Due to its Cr, Mo, W, and V alloying, it retains its hardness and wear resistance at temperatures up to 600°C. It is used on unalloyed steels, in the production of cold and hot cutting tools, and in the welding and surfacing of cutting edges. It provides a stable arc and smooth weld bead.Typical Applications: Highly suitable for hardfacing of hot forging die

EN 14700

T Fe8

TS EN 14700

T Fe8

DIN 8555

MF 6-GF-60-GP

High alloy and high hardness flux cored wire, especially used for hardfacing welds of parts subject to high metal-to-metal frictional wear and medium impact. The weld metal has high toughness and crack resistance and is resistant to shocks and impacts. The weld metal maintains its hardness at working temperatures up to 600°C. The weld metal can be machined with stone or carbide inserts. For high carbon and low weldability materials, a buffer layer with FCW 30 is recommended before hardfacing. Heat treatment reduces the hardness after welding. Typical Applications: Hardfacing of hot cutting and stripping blades, die casting molds, separator and shredder blades, conveyors, rollers, crusher rolls, parts of earth-moving machines, bucket lugs and wear parts of agricultural tools.

EN 14700

T Fe3

EN 14700

~T Fe14

TS EN 14700

~T Fe14

DIN 8555

MF 10-GF-65-GR

Self-shielded flux-cored wire designed for hardfacing parts exposed to severe abrasive wear and low impact. The weld metal has high hardness due to its high chromium carbide content and can only be machined by grinding. Transverse cracks that may occur in the weld bead do not reduce wear resistance. A maximum of three layers is recommended. Typical Applications: Hardfacing of wear plates made from carbon steels, low/high alloy steels, or Ni-Hard materials. Suitable for bucket teeth and crusher picks of earth-moving machinery, screw conveyors, mixer fan blades, and crushers.

EN 14700

~T Fe7

TS EN 14700

~T Fe7

DIN 8555

MF-5-GF-200-C

Gas shielded flux cored wire for surfacing and buffer layer application on parts, subjected to metal-to-metal wear (adhesion), moderate impact, thermal fatigue and corrosion. Especially designed for buffer layer application, in order to reduce dilution and crack suseptibility of new continue casting rollers, at the top part of the line. Provides smooth and easily machinable surface on stringer weld bead or weaving technique.Typical Applications: Suitable for buffer layer on new continue casting rolls, before hardfacing layers. Also suitable for surfacing of steam turbines, valves and valve seats.

EN 14700

T Fe10

TS EN 14700

T Fe10

DIN 8555

MF 8-GF-200/400-KPZ

Gas shielded flux cored wire, providing 18Cr - 8Ni - 7Mn austenitic stainless steel weld metal. Used for buffer layer applications and joining of 14% Manganese steels to high manganese steels, stainless steels and carbon steels. Additionally, it is well-suited for buffer layer application on 14% Mangganese steels. Due to it's high crack resistant weld metal, suitable for joining dissimilar steels, difficult-to-weld steels, armor plates and buffer layer application in crack sensitive large sections before hardfacing.Typical Applications: Used for joining wear plates to bucket, joining bucket teeth, joining and surfacing of rails, switch points, crossovers and press arms.

EN 14700

T Fe10

TS EN 14700

T Fe10

DIN 8555

MF 8-GF-200/400-KPZ

Open arc flux cored wire, providing 18Cr - 8Ni - 7Mn austenitic stainless steel weld metal. Used for joining 14% Manganese steels and 14% Manganese steels to stainless steels and carbon steels. It is well-suited for buffer layer application on 14% Manganese steels. Due to it's high crack resistant weld metal, suitable for joining dissimilar steels, difficult-to-weld steels, armor plates and buffer layer application in crack sensitive large sections before hardfacing.Typical Applications: Used for joining wear plates to bucket, joining bucket teeth, joining and surfacing of rails, switch points, crossovers and press arms.